In this the study, polyester/cotton(P/C) blended fabrics with fine denier were developed to get the light weight compared with the traditional P/C blended fabrics. Moreover, the width of the fabrics was extended by the tenter during the final heat treatment to get the lower fabric density and lighter weight. Then, the physical properties of these fabrics were analysed. The results were as the follows: The developed fabrics had 22.6-31.6% lighter weight than the traditional fabrics with the same fabric width. The weight of fabric decreased drastically with the fabrics width down to 67.1 $g/m^2$. The fabric density for the warp direction decreased with the fabric width. The tenacity and the elongation of the developed fabrics was little lower than that of the traditional fabrics. The air permeability of the developed fabrics increased with that of the traditional fabrics. The stretch rate of the developed fabrics decreased with increasing the fabric width. Residual stretch rate of the developed fabrics was more stable than that of the traditional fabrics. Residual stretch rate of the developed fabrics increased with the fabric width, but the highest value was less than 5% which is quit stable.