The $(Sr_{0.85}Ca_{0.15})TiO_3(SCT)$ thin films were deposited on Pt-coated electrode $(Pt/TiN/SiO_2/Si)$ using RF sputtering method according to the deposition condition. The crystallinity of SCT thin films were increased with increase of deposition temperature in the temperature range of $100{sim}500[^{circ}C]$. The optimum conditions of RF power and $Ar/O_2$ ratio were 140[W] and 80/20, respectively. Deposition rate of SCT thin films was about $18.75[{AA}/min]$ at the optimum condition. The composition of SCT thin films deposited on Si substrate is close to stoichiometry (1.102 in A/B ratio). The maximum dielectric constant of SCT thin film as obtained by annealing at $600^{circ}C$.