A suspension polymerization of styrene In aqueous phase was employed to study if polystyrene particles ranging from 1 to $20{mu}m$ can be produced. Hydrophobic silica was selected as a stabilizer and azo-bisisobutyronitrile (AIBN) as an initiator. Polymerization reaction was carried out at a selected temperature in the range of $65{sim}95^{circ}C$. Stabilizer concentration was varied from 0.17 to 3.33 wt% compared to the water while the concentration of the initiator was raised from 0.13 to 6.0 wt% compared to the monomer. Dispersion of hydrophobic silica into the water phase was achieved by precise control of pH. Optimum dispersion of silica was obtained at pH 10. Average particle diameter decreased with increasing amounts of stabilizer concentration initially, exhibiting the minimum average diameter at 1.67 wt% of stabilizer concentration, after which it started to Increase. It is speculated that an excessive presence of stabilizer encouraged a secondary reaction in the reaction medium, which led to particle agglomeration, and as a result an increase in average particle diameter. Molecular weight was found to be independent of stabilizer concentration between 0.13 and 1.00 wt% whereas, it increased when stabilizer concentration exceeded 1.67 wt%. Variation of molecular weight was probably caused by the reduced activity and efficiency of initiator due to the high concentration of silica, and the secondary reaction in the reaction medium, as well. An increase in the Initiator concentration and/or reaction temperature resulted in an increase in both reaction rate and particle diameter. Consequently, we have confirmed that spherical polystyrene particles with $1{sim}20{mu}m$ in diameter can be prepared by careful selection of the concentration of stabilizer, initiator, pH and reaction temperature.