The reduction behavior of $TiO_{2}$ in Al and Al/CaSi containing self-reducing $TiO_{2}$ briquettes(SRTB) was investigated. The maximum yield of Ti was expected with the slag composition of 45-55%CaO in the $CaO-Al_{2}O_{3}$ system. When $CaCO_{3}$ was used as a flux, the oxidation loss of reducing agent by $CO_{2}$ should be compensated, and therefore it leads to excessive requirement of the reducing agent. By using Al and CaSi mixture as a reducing agent of $TiO_{2}$, the reaction products both oxide and metal could be liquefied, and separated effectively with each other. As a result, the yield of Ti increases remarkably. The optimum mixing ratio of CaSi to Al is 78%CaSi-22%Al.????????2??N?????????