Due to the diversified use of recent Piezoelectric Zirconate Titanate Composite Actuate. (PZTCA), various PZTCAs with the different ply orientation of the fiber layer have been applied. For this reason, the applicable bending moment equation is necessary even though the fiber layer ply orientation and the laminate configuration are changed. The aim of this research is to evaluate the relationship between the total effective moment $(M^E)$ and Bernoulli-Euler bending moment (M) when the ply orientations of UD CFRP are changed. In conclusions, firstly, as the performance test results by the CFRP ply orientation, the performance of [0] and [90] were stable. However, while the performance of [+45] was suddenly decreased after 5 hours. Secondly, the change of $(M^E)$ by the CFRP ply orientation was evaluated. As the CFRP ply orientation was increased from [0] to [+60], the $(M^E)$ were gradually decreased. However, they became a little bit increased from [+60] to [90]. Finally, after the change of M by the CFRP ply orientation was evaluated, it was found that $M^E=2.2M$ was valid for just [0] and that there was a relationship between $M^E$ and M according to the ply orientation.