In our angle configuration, several peculiar characteristic behaviors of MR could be observed, the mixing of positive MR(PMR) and negative MR(NMR) in the inclined sample was observed. The complete mixing angle, ${phi}_{mix}$ as a function of inclination angle, ${ heta}$ was observed to fit well to the relation of ${phi}_{mix}=tan^{-1}(1+tan{ heta})$ in nickel films. The above theoretical relation was obtained by decomposing the magnetic field into the components parallel and perpendicular to the current flow and identifying ${phi}_{mix}$ as the angle satisfying that the above two components of magnetic field were identical. We also observed that the data of ${phi}_{mix}$ did not satisfy the above theoretical relation in the iron film. This was explained by the fact that the growth direction in the iron film was an intermediate direction of magnetization, while the growth direction in the nickel film was an easy axis of magnetization.