폐콘크리트 파쇄시 발생하는 재생잔골재의 품질을 검토하였으며, 재생잔골재를 활용한 모르타르의 압축강도, 휨강도 및 흡수율을 검토하였다. 또한, 프리캐스트 콘크리트 제품용 골재로서의 적용성에 대하여 평가하였다. 재생잔골재의 밀도 및 흡수율은 각각 $2.31;g/cm^3$ 및 8.07%로 KS F 2573의 2종에 해당되는 품질이었다. 혼합시멘트 MRS1, MRS2 및 MRS3 사용 모르타르의 재령 28일 압축강도는 물-시멘트비 35%, 양생온도 $40^{circ}C$의 조건에서 각각 15.8, 27.4 및 48.7MPa로 최대값을 발현하였다. 모르타르의 최대휨강도는 혼합시멘트 MRS1 및 MRS2 사용시 물-시멘트비 35.0%, 양생온도 $40^{circ}C$, 혼합시멘트 MRS3사용시 물-시멘트비 37.5%, 양생온도 $40^{circ}C$의 조건에서 발현하였다. 혼합시멘트 MRS1, MRS2 및 MRS3를 사용한 모르타르의 흡수율의 범위는 각각 $8.3{sim}7.3%,;6.5{sim}8.5%$ 및 $3.5{sim}6%$의 범위로 나타났다. 그러므로 혼합시멘트와 재생잔골재의 비율을 적절히 조절함으로써 MRS1는 저강도용, MRS2는 보통강도용, MRS3는 고강도용으로 다양한 프리캐스트 콘크리트 제품에 적용될 수 있을 것으로 기대된다.
The duality of recycled fine aggregate (RS) which was produced at the waste concrete crushing was investigated. The compressive strength, flexural strength and absorption of mortar utilized with RS were examined. It was evaluated on the application of RS as precast concrete aggregate. The density and absorption of RS were $2.31g/cm^3$ and 8.07% respectively, the quality of RS was satisfied with the criterion of KS F 2573 type 2. The maximum 28days compressive strength of mortar mixed with blended cement MRS1, MRS2 and MRS3 were developed with 15.8, 27.4 and 48.7MPa respectively, in condition to curing temperature $40^{circ}C$ and water-cement ratio 37.5%. When blended cement MRS1 and MRS2 were used, the maximum flexural strength of mortar was developed at curing temperature $40^{circ}C$ and water-cement ratio 35.0%. When blended cement MRS3 was used, the maximum flexural strength of mortar was developed at curing temperature $40^{circ}C$ and water-cement ratio 37.5%. The absorption of mortar mixed with blended cement MRS1, MRS2 and MRS3 were indicated the range of $8.3{sim}7.3%,;6.5{sim}8.5%$ and $3.5{sim}6%$ respectively. Therefore, when the ratio of blended cement and RS is appropriately centre]led, it would be expected that MRS1, MRS2 and MRS3 will be able to apply the variable low strength, medium strength and high strength precaste concrete.