In this study, the sputtered BTO film was polished by CMP process with the self-developed $BaTiO_3$- and $TiO_2$-mixed abrasives slurries (MAS), respectively. The removal rate of BTO ($BaTiO_3$) thin film using the $BaTiO_3$-mixed abrasive slurry (BTO-MAS) was higher than that using the $TiO_2$-mixed abrasives slurry ($TiO_2$-MAS) in the same concentrations. The maximum removal rate of BTO thin film was 848 nm/min with an addition of $BaTiO_3$ abrasive at the concentration of 3 wt%. The sufficient within-wafer non-uniformity (WIWNU%) below 5% was obtained in each abrsive at all concentrations. The surface morphology of polished BTO thin film was investigated by atomic force microscopy (AFM).