Ni-Cu-Zn ferrites were prepared by the co-precipitation. Physical properties and Microwave absorbing properties were investigated in Ni-Cu-Zn ferrite for the aim of microwave absorbers. From the analysis of X-ray diffraction patterns, we can see that all the particles have only a single phase spinel structure. The loss factor was maximum at sintering temperature $1100^{circ}C$. The initial permeability of sintered ferrite obtained was an average of 50. We found that the $(Ni_{0.7}Cu_{0.2}Zn_{0.1}O)_{1.02}(Fe_2O_3)_{0.98}$ can be used in ferrite rubber composite microwave absorber when sintering temperature at $1100^{circ}C$.