This study was focused on the effect of sintering additive and particle size on the low temperature sintering of $0.85CaWO_4-0.15SmNbO_4$ ceramics. With an increase of $CaV_2O_6$ content, the sintering temperature of the specimens was reduced from $1150^{circ}C;to;800^{circ}C$. The dielectric constant (K) and Qf value were increased with $CaV_2O_6$ content. These results are due to the enhancement of the density by the liquid phase sintering. Temperature coefficient of resonant frequency (TCF) was slightly shifted to the positive value with $CaV_2O_6$ content. Typically, K of 12.64, Qf of 23,106 GHz, TCF of $-34ppm/^{circ}C$ were obtained for the specimens with 7 wt.% $CaV_2O_6$ sintered at $900^{circ}C$ for 3 h.