Cobalt titanates($CoTiO_x$), such as $CoTiO_3$ and $Co_2TiO_4$, have been synthesized via a solid-state reaction and characterized using X-ray diffraction(XRD) and X-ray photoelectron spectroscopic(XPS) measurement techniques, prior to being used for continuous wet trichloroethylene(TCE) oxidation at $36^{circ}C$, to support our earlier chemical structure model for Co species in 5 wt% $CoO_x/TiO_2$(fresh) and(spent) catalysts. Each XRD pattern for the synthesized $CoTiO_3$ and $Co_2TiO_4$ was very close to those obtained from the respective standard XRD data files. The two $CoTiO_x$ samples gave Co 2p XPS spectra consisting of very strong main peaks for Co $2p_{3/2}$ and $2p_{1/2}$ with corresponding satellite structures at higher binding energies. The Co $2p_{3/2}$ main structure appeared at 781.3 eV for the $CoTiO_3$, and it was indicated at 781.1 eV with the $Co_2TiO_4$. Not only could these binding energy values be very similar to that exhibited for the 5 wt% $CoO_x/TiO_2$(fresh), but the spin-orbit splitting(${Delta}E$) had also no noticeable difference between the cobalt titanates and a sample of the fresh catalyst. Neither of all the $CoTiO_x$ samples were active for the wet TCE oxidation, as expected, but a sample of pure $Co_3O_4$ had a good activity for this reaction. The earlier proposed model for the surface $CoO_x$ species existing with the fresh and spent catalysts is very consistent with the XPS characterization and activity measurements for the cobalt titanates.