In the present study, we investigated the formation of self-organized nanostructure oxide layers on CP Ti and Ti-10Ta-10Nb alloy in an electrolyte of 1M phosphoric acid and 1.5 wt% Hydrofluoric acid. The morphology of oxide film on substrate was observed using scanning electron microscopy and transmission electron microscopy The surface roughness of titanium oxide film was analyzed by atomic force microscopy and the crystalline of specimen was investigated using X-ray diffractometer. The results of this study showed that well-aligned titanium oxide nanotubes are formed with diameter of approx. 100nm and length of approx. 500nm with CP Ti. However, it is clear that TiTaNb alloy highly irregular structure with various diameters. Transmission electron microscope investigations show that the specimens were confirmed as amorphous. Such titanium oxide nanotubes are expected a well-adhered bioacitive surface layer on titanium substrate for orthopedics and dental implants.