This study was performed to evaluate strength and watertightness properties of EVA modified high strength concrete in order to improve durability of concrete used in agricultural water utilization facilities that are in constant contact with water. Materials used were cement, coarse and fine aggregates, silica fume, EVA and AE water reducing agent. Tests for the slump, compressive and flexural strengths, absorption ratio and permeability coefficient according to curing condition (water and water+dry curing) and content ratio of EVA were performed. The slump results of EVA modified high strength concrete similarly showed in the content ratio of EVA powder less than 4% and decreased in the content ratio of EVA powder more than 6% compared to that of concrete without EVA powder. The compressive strength of EVA modified high strength concrete decreased with increasing the content ratio of EVA powder. The flexural strength of EVA modified high strength concrete increased with increasing the content ratio of EVA powder in the content ratio of EVA powder ratio less than 4% and had similar or slightly decreased in the content ratio of EVA powder more than 6% compared to that of concrete without EVA powder. The absorption ratio and permeability coefficient of EVA modified high strength concrete decreased with increasing the content ratio of EVA powder in the content ratio of EVA powder less than 4% and slightly increased in the content ratio of EVA powder more than 6%.