General criteria for the risering design of steel castings and commercial codes for the flow and solidification analysis were used to design the optimized risering in V-process. Three type of specimens were chosen including thin plates and a thick disc. Sided riser installed in the front of a plate casting was effective to prevent the shrinkage defects and to increase the casting yield ratio. Exothennic sleeve and chill were also effective. It was possible to apply the general criteria for the risering design of steel castings to V-process. Temperature of a mold surface was expected to rise over $1,000^{circ}C$ in the temperature calculation considering radiation effect of molten metal in the mold. Since weakening temperature of the vinyl used in V-process is about $70^{circ}C$, it should be emphasized that a proper coating of the vinyl film is necessary to prevent the possibility of burning out of the vinyl by the molten metal.