A lot of fatigue tests on a material, JIS SM490A, with yielding strength of about 350 MPa and tensile strength of about 520 MPa were carried out. Various butt-welded specimens such as reinforcement removed, as-welded and weld toe ground, several types of fillet-welded specimens and full-size box type components were used. After having obtained S-N curves for the above- mentioned specimens, fatigue strengths were compared to those of foreign design codes, AWS, BS 7608 and ENV. It was found the fatigue strengths at low cycles are not in a good agreement with the foreign codes, but the fatigue limits are in a good agreement.