This study investigates the engineering properties of concrete incorporating lime stone crushed fine aggregate(Ls), which has been abandoned about 20% of total production due to the low purity. Test results showed that increase of Ls had favorable fluidity and slightly decreased air content. Bleeding capacity of all specimens was not appeared as those were high strength mixture proportion, but the specimens using more Ls accelerated initial and final setting. For the mechanical properties, specimens incorporating higher ratio of Ls, overall, resulted in increase of compressive strength, and exhibited very small inclined tendency in a dynamic elasticity modulus test In addition, for the durability properties, specimens incorporating higher Ls dramatically decreased a drying shrinkage and showed similar tendency in a frost & thaw test, as well as showing no more change in an accelerated neutralization test from the beginning. In conclusion, as it was confirmed in the experimental test, the high strength concrete applying Ls did not showed any problems in the aspects of engineering properties and mostly exhibited even more excellent quality than the specimens using natural fine aggregate.