Kevlar was chemically surface modified with resorcinol-formaldehyde(RF) prepolymer and VP rubber latex for application to high strength tirecords. RF prepolymer was easily obtained by polymerization at room temperature in the presence of a base catalyst. The mechanical and thermal properties of Kevlar were not significantly changed during surface treated under various conditions. The change of adhesion with rubber were investigated through H-test method. Maximum increase of adhesion force between rubber and Kevlar was obtained up to 40% than that of untreated one when the fiber was soaked in RFL dipping solution and thermally treated at $170^{circ}C$ for 3 - 5min.