Microstructure and tensile strength of the vacuum brazed stainless steel were investigated in this study. For vacuum brazing of the stainless steel 303 and 304, the BNi-2, 3, 4 and 7 were used as filler metals. Among these filler metals, the BNi-2 showed excellent wettability at $1050^{circ}C$. Indeed, the brazed stainless steel using the BNi-2 showed the highest tensile strength (483 MPa) among all brazed specimens. This is attributed to degree of interfacial reaction between the filler metal and stainless steel. Brazed stainless steel with BNi-2, 3 filler metals showed almost elastic deformation followed by plastic yielding and strain hardening up to a peak stress. On the other hand, it is likely that the fracture of the brazed specimens with BNi-4, 7 was occurred in elastic range without plastic yielding up to a peak stress.