Fe based SOFC(Solid Oxide Fuel Cell) interconnector was fabricated by using the spark plasma sintering process and its microstructure and mechanical properties were investigated in this study. To fabricate the interconnector, the Fe-26Cr powder was mixed with the Ag (5, 10, 20wt.%) particles. In the Fe-26Cr-Ag sintered bodies, the Ag particles were almost dispersed at the grain boundary of the Fe-26Cr. The sintered bodies have the density of 87.2-97.5%, the density increases with increasing Ag content at sintering temperature of $850^{circ}C$. Also, the compressive yield strength increases with increasing Ag content at the same sintering temperature.