Thermal conductivities in $La_2Ce_2O_7-Gd_2Ce_2O_7-Y_2Ce_2O_7$ ternary system have been investigated. Pyrochlore phases formed at all ternary compositions and their sinterbilities were decreased with La addition. Thermal conductivities showed a minimum value at $La_2Ce_2O_7$ with moderate increases as $Y^{3+}$ and $Gd^{3+}$ ions replaced $La^{3+}$. Thermal expansion anomaly observed in $La_2Ce_2O_7$, which might be detrimental to TBC application, were suppressed by $Y^{3+}$ and $Gd^{3+}$ additions, with resultant thermal conductivities, $1.3{sim}1.5 W/mK$ at $1000^{circ}C$.