Hot-dip galvannealed sheet (GA) with high strength of 590MPa grade in tensile strength, has developed for automotive applications. However, for a successful application, the microstructure and galvannealing behavior of galvannealed TRIP steel sheets must be strictly controlled. High silicon contents steel has problems with weld-ability, zinc coating and reduction of retained austenite volume fraction after galvannealing process. The main purpose of this study is to solve the problem as indicated above.