In this paper, the gas responses of tungsten oxide films prepared by anodic reaction was discussed. Sensing electrodes and heating electrodes were patterned by photolithography method on quartz substrate. Porous tungsten oxide was fabricated in electrolyte solutions of 5 % HF (HF :$C_2H_6OH:H_2O$=3 : 2 : 20) by anodic reaction. The anodic reaction with metal (platinum wire) as a cathode and the sensing device as an anode was conducted under the various reaction times (1-10 min) at 10 mA/$cm^2$ The surface structure and morphology of the fabricated sensor have been analysed by X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM). All the peaks of XRD results were well indexed to the pure phase pattern. The average diameter of the porous tungsten oxide surface were ranged about 100 nm. The fabricaed sensor showed good sensitivity to 200 ppm toluene at operating temperature of $250^{circ}C$.