The short-term high temperature creep rupture behavior of Ni-based Alloy718 steel was investigated at the elevated temperatures range of 550 to $700^{circ}C$ under constant stress conditions. The creep rupture characteristics such as creep stress, rupture time, steady state creep rate, and initial strain were evaluated. Creep stress has a quantitative correlation between creep rupture tim and steady state creep rate. The stress exponents (n, m) of the experimental data at 550, 600, 650 and $700^{circ}C$ were derived as 33.5, -24.9, 26.1, -21.2, 16.8, -12.8 and 10, -8.2, respectively. The stress exponent decreased with increasing creep temperature. The creep lift prediction was derived by the Larson-Miller parameter (LMP) method and the resultant equation was obtained as follows: T($logt_r$+20)=-0.00252 ${sigma}^2$-1.377${sigma}$+-22718.