Cotton, wool, cotton/wool blended (80:20) and tencel fabrics were treated with low temperature oxygen plasma, enzymes (cellulase or protease), or oxygen plasma-enzyme and they were examined for dyeing and handling properties for environment friendly finishing. The appropriate conditions for cellulase treatment were enzyme concentration of 3g/l, pH of 5, and $60^{circ}C$ for one hour, and for protease treatment were enzyme concentration of 4g/l, pH of 8, and $60^{circ}C$ for one hour. The equilibrium uptake of a direct dye on cotton changed with plasma treatment and plasma-cellulase treatment, and the rate of dyeing slightly decreased. When wool was dyed with acid dye, the equilibrium dye uptake did not change with plasma, protease treatment nor plasma-protease treatment, however, the rate of dyeing had increased with plasma-protease treatment. From these results, it is assumed that plasma attacks the surface of the fiber, and enzyme mainly affects the inner part of the fiber. Plasma treatment did not affect mechanical properties related to the handling of fabrics. The handling test showed increased extension at maxmum load(EM), tensile energy(WT) with decreased tensile resilience (RT), and the fabrics became softer but resilience decreased slightly with enzyme treatment. The bending recidity(B), hysteresis of bending moment(2HB), and hysteresis of shear force at five degrees(2HG5) decreased, however, shear stiffness(G) increased. I knew the plasma pre-treatment made fabrics softer with lower koshi(stiffness). The handling of plasma pre-treated fabrics was better than that of enzyme-treated fabrics. When we pre-treated fabrics, the handling test showed decreased coefficient of friction(MIU), geometrical roughness(SMD), while the surface of fabrics became smoother and numeri increased. Even though compression resilience(RC) increased, fukurami(bulky property) and compressive elasticity, decreased due to the linearity of compression-thickness curve(LC) and compression energy(WC).