This study was conducted to made a grid alloy (Pb-Ca-Sn-Al) which has a temporary composition ratio in order to improve the efficiency of lead acid batteries. The positive activity material made a 3BS(tri-basic lead sulfate; $3PbO{cdot}PbSO_4{cdot}H_2O$) by a low temperature curing and it evaluates the plate efficiency through the life cycle testing. The initial current capacity of low temperature curing plate was excellent but the life cycle was not good (S1). As for the S2 plate, however, the initial current capacity and the life cycle were superior.