[ $B_4C$ ] ceramics were fabricated by spark plasma sintering process and their sintering behavior, microstructure and mechanical properties were evaluated. Relative density of $B_4C$ ceramics could be achieved by spark plasma sintering method reached as high as 99% at lower temperature than conventional sintering method, in addition, without any sintering additives. The mechanical properties of $B_4C$ ceramics could be improved by the heat treatment at $1300^{circ}C$ during sintering process which can be removed $B_2O_3$ phase from a $B_4C$ powder surface. This improvement results from the formation of a fine and homogeneous microstructure because the grain coarsening was suppressed by the elimination of $B_2O_3$ phase. Particularly, mechanical properties of the specimen experienced the $B_2O_3$ removing process improved over 30% compared with the specimen without that process.