Purpose: To observe the high temperature creep test and the fracture surface of the samples of 9% Ni alloy steel generally used for all kinds of mahine parts and predict the durability of that by determining a constant of C with a Larson-Miller variable. Methods: The equipment of this test was made into lever-beam style designed by Andrade and F. Garofalo et al.. The condition of creep test was set under 16 kinds of conditions after fixing 4 kinds of temperature condition and 4 kinds of stress condition to check how it effects the samples. Results: The temperature of creep test was increased, the stress index (n) of creep deformation was gradually decreased from 3.97 to 3.55. The activation energy of creep deformation was decreased from 90.39 to 83.64 kcal/mol when the stress was increased. A constant of C value by calculation of larson-Miller variable was about 22 and if temperature for use is suggested, the durability could be calculated. Conclusions: By analyzing the fracture phenomenon and suggesting the observation result of the fracture surface of the samples and creep test of 9% Ni alloy steel, the basic design data for the practical use of accessories in the field of equipment could be constructed and used to predict the durability of the equipment.