In this paper, we investigated the (002) preferred orientation and morphology characteristics of AlN thin film by using reactive rf sputtering. Additionally, AlN thin films grown in the range from 150 to 300 W were studied under room temperature without substrate heating and post annealing. Sputtered AlN thin films were well grown on Si substrates and the (002) main peak in XRD patterns showed the highest intensity at 300 W with $0.25^{circ}$ degree of full width at half-maximum (FWHM). As increased RF power, the surface roughness was increased from 1.0 to 3.4 nm. In Fourier transformation infrared spectroscopy (FTIR), $A_1$ (TO) and $E_1$ (TO) mode closed to AlN thin film confirmed the changes with increasing the intensity rate. From these results, we could confirm a chance of the growth of AlN thin film by only low temperature.