Nano-sized $TiO_2$-60 wt% SrO composite powders were synthesized by a sol-gel method using titanium isopropoxide and $Sr(OH)_2;{cdot};8H_2O$ as precursors. 3, -5, -7 wt%Ag spot-coated $TiO_2$-60 wt% SrO composite powders were synthesized by a Ag electroless deposition method using $TiO_2$-60 wt% SrO composite powders calcined at $1050^{circ}C$, which mainly exhibited the $SrTiO_3$phase. However, a small number of rutile $TiO_2$, $Sr_2TiO_4$ and $SrO_2$ phases were also detected. In the Ag spot-coated powders synthesized by electroless deposition, nano-sized particles about 5-25 nm in diameter adhered to the $TiO_2$-60 wt% SrO composite powders. The photocatalytic activity of Ag spot-coated $TiO_2$-SrO and $TiO_2$-SrO composite powders for degradation of phenol showed that all of $TiO_2$-SrO composite powders were highly active under UV light irradiation. 7 wt%Ag spot-coated $TiO_2$-60wt.%SrO composite powders had a relatively higher photocatalytic activity than did $TiO_2$-SrO composite powders under visible light.