Three kinds of 135D/108F ITY were produced from raw yam 85D/72F + SDY 50D/36F with. interlacing pressure $1.5kg/cm^2$, $2.5kg/cm^2$, $3.5kg/cm^2$ respectively. 72 kinds of sized yams were manufactured from three ITYs by altering sizing speed, sizing temperature and sizing tension. The mechanical characteristics of 72 kinds of plain fabrics which were woven using the sized yam as a warp were analyzed after scouring. The initial modulus of scoured fabric responded sensitively to the sizing speed in high tension. The WT of scoured fabric recorded the. highest1n the conditions of sizing tension 30g, and air pressure $2.5kg/cm^2$ in interlacing treatment. When sizing temperature was high, the WT value appeared low, but when sizing speed was high, the WT value was much affected by air pressure in interlacing raw yam. The MIU value of fabric according to sizing tension variations increased up to sizing tension 40g, but decreased above it. The bulk density decreased up to sizing tension 30-40g, but increased above it. In addition, the bulk density decreased as sizing temperature increased.