Purpose : This study sought to examine the aspects of crestal bone resorption and to evaluate the clinical outcomes of the TiUnite$^{(R)}$ (Nobel Biocare, Sweden) anodized implant system. Materials and Methods : Among the 67 patients (211 fixtures) who were treated using TiUnite(r) implants at Seoul National University Bundang Hospital between March 2004 and January 2007, 26 (91 fixtures) were considered in this study. Initial and secondary stabilities were measured using Periotest$^{(R)}$ and Ostell(tm) Mentor. The radiographic evaluation of crestal bone resorption was carried out by measuring the change in crestal bone level at the time of surgery compared to that 1 year after loading. Panoramic radiograph and periapical radiograph were used. Based on the radiographic findings, the shapes of crestal bone resorption were classified. Results : The average amount of crestal bone resorption after 1 year of functional implant loading was 0.30 mm. There was no saucerization in 40 implant fixtures (43.9%), although more than 1 thread were exposed in 51 implant fixtures (56.6%). The success rate of the implants was 94.5%, and the survival rate was 100%. Conclusions : Good clinical outcomes and minor crestal bone resorption were noted in this study. Saucerization for the establishment of biological width was not a general finding in the TiUnite$^{(R)}$ anodized implant system.