Various Sialon ceramics were fabricated by hot-pressing mixtures of $Si_3N_4$ with additive $Y_2O_3$ and $Al_2O_3$. The polished specimen of SiAlON $I{sim}III$ went on increasing in strength by heat treatment, heat treated non-polished specimen were similar or up to polished specimen in strength. The polished specimen of both SiAlON IV and V showed a very high strength, but were not Increasing of strength by heat treatment. All specimens were fractured on the surface and at the inner flaws. Surface fractures were initiated from the polished surface flaw and corner flaw. Inner fractures were initiated from an internal defect.