This study was to evaluate the biaxial flexural strength of zirconia ceramics after glass-infiltration on zirconia core. The zirconia specimens were made with diameter-15mm, thickness-0.6mm using zirconia block which divided into 1) sintered group, 2) heat - treated group, 3) Glass - infiltrated group and experimented fracture strength by each 10 specimens in experimental group. The biaxial flexural test was performed at crosshead speed of 0.1${eta};{AE}$ min. The experiment result average fracture strength was shown 541.0${eta}acute{A}$ in sintered group and glass-infiltrated group as 662.2${eta}acute{A}$ river of 22.4% rise appear. Weibull coefficient sintered group is 3.462 and glass-infiltrated group improved believability about fracture strength from melting permeation processing of glass by 4.716.