The effect of $LaF_3$ coating on the structural and electrochemical properties of $Li[Ni_{0.3}Co_{0.4}Mn_{0.3}]O_{2}$ cathodes was investigated using XRD, SEM, TEM, and a cycler. The coating layer consisted of nano-sized particles attached nonuniformly to the surface of pristine powder. Despite the surface coating treatment, phase difference by $LaF_3$ coating was not detected. The discharge capacities of coated electrodes were a little lower than that of pristine sample at a 1 C rate. However, as the C rate increases, the capacity retention of the coated sample becomes obviously superior to that of the pristine sample. The cyclic performances of the electrodes in the voltage range of 4.8 $sim$ 3.0 V were also improved by the surface coating. Such enhancement is attributed to the presence of the $LaF_3$ coating layer, which effectively suppressd the reaction between electrodes and electrolytes on the surface of the $Li[Ni_{0.3}Co_{0.4}Mn_{0.3}]O_{2}$ electrode.