In this study, it is experimentally verified a feasibility of the wasted phosphogypsum ($CaSO_4/H_2O$) that is a byproduct from the phosphoric acid process of manufacturing fertilizers can be applied as an admixture in slag cement. For the test, phosphogypsum is modified as dihydrate, hemihydrate, type III anhydrite, and type II anhydrite, and then chemical characteristics and mechanical properties of various slag cements containing above mentioned gypsum materials were analyzed. The test results show that the gypsum made at high temperature has better quality with decrease of water-soluble phosphoric acid ($S-P_2O_5$) which has an effect on the quality of cement. And type II anhydrite shows superior quality in terms of drying shrinkage and the compressive strength of cement paste with hemihydrate at 56 days is higher than other gypsum material.