The low-temperature preparation of porous ceramics was carried out using mixtures of alumina-zinc borosilicate (ZBS) glass. The compositions of alumina-ZBS glass mixture with PMMA pore-former were unfortunately densified. Because PMMA was evaporated below the softening point of ZBS glass ($588{^{circ}C}$), the densification through the pore-filling caused by the capillary force might occur. Howerver, those with carbon possessed pores where carbon was evaporated above the softening point. The porous ceramic having 35% porosity was successively fabricated by the low-temperature sintering process below $900{^{circ}C}$ using 45 vol% of alumina, 45 vol% ZBS of glass, and 10 vol% of carbon as starting materials.