Nano-porous $TiO_2$ powder was fabricated using Acetylene black, applied photo voltaic device based on the Dye-sensitized Solar Cells (DSCs) was investigated experimentally. $TiO_2$-powder was fabricated using Ti-isopropoxide and 2-propanol by sol-gel combustion method. For cases of variable Acetylene black, characteristic of porosity, size of particle and crystallite of obtained $TiO_2$ nano-powder was investigated. The photovoltaic efficiency of the prepared DSCs was measured using $TiO_2$ film which prepared on each different heat treatment temperature($400^{circ}C{sim}700^{circ}C$) with paste of $TiO_2$ powder. The porosity and size of particle of $TiO_2$ powder made with Acetylene black 0.4g was influenced significantly effect to DSCs characteristic. Heat treatment at $500^{circ}C$ makes the better photovoltaic efficiency which 5.02%($J_{sc}=11.79mA/cm^2$, $V_{oc}=0.73V$, ff=0.58). The sol-gel combustion method was useful to DSCs fabrication.