본 연구에서는 직물 탄소/에폭시와 유리/에폭시의 DCB(double cantilever beam)시편을 제작하여 ASTM 5528-01에 준하여 모우드 I 층간파괴인성을 측정하고, 이와 동일한 조건의 유한요소해석을 수행하여 층간파괴거동을 해석적으로 평가하였다. 시험에 의하여 측정된 층간파괴인성은 탄소/에폭시는 평균 $845.7J/m^2$, 유리/에폭시는 $1,042J/m^2$였다. 유한요소 모델은 접착요소를 이용하여 층간파괴를 구현하였고, 측정된 층간파괴인성을 부여하였다. 해석 결과의 검증을 위하여 시험을 통하여 측정된 시편 끝단의 반력과 Timoshenko 빔 이론을 통하여 계산된 결과를 비교하였다. 측정된 결과와 해석결과는 유사하였다.
In this study, DCB(double cantilever beam) specimens of woven fabric carbon/epoxy and glass/epoxy were manufactured and mode I fracture toughness of specimen was measured according to ASTM 5528-01. And FE analysis was conducted in the same condition and evaluated the behavior of delamination analytically. Mode I fracture toughness measured by test was $845.7;J/m^2$ in the case carbon/epoxy and that of glass/epoxy was $1,042;J/m^2$. FE analysis was conducted using cohesive elements for adhesive layer and applied measured fracture toughness. To verify the result of analysis, the reaction force measured at the end of specimen and that calculated by Timoshenko beam theory were compared. The numerical results show good agreements with the measured one.