Selective area epitaxy of multiple-stacked InP/InGaAs structures were grown by chemical beam epitaxy. The width of top of the multiple-stacked InP/InGaAs layer which were selectively grown on the stripe lines parallel to the <011> direction was narrowed, while the width of top of the multiple-stacked InP/InGaAs layer on the stripe lines parallel to the <01-1> was widen. This difference according to the <011> and <01-1> direction was explained by the growth of InGaAs <311>A and B faces on the (100) InP surface on the stripe lines parallel to the <01-1> direction. Under growth rate of $1;{mu}m/h$, top of the multiple-stacked InP/InGaAs was flattened as the pressure of group V gas was decreased. This phenomenon was understood by the saturation of group V element on the surface.