$(Ba_{0.57}Sr_{0.33}Ca_{0.10})TiO_3$(=BSCT) powders, prepared by the sol-gel method, were doped using $MnCO_3$ as the acceptor and $Dy_2O_3$ as the donor. This powder was mixed with an organic vehicle. BSCT thick films were fabricated by the screen-printing techniques on the alumina substrate. The structural and dielectric properties of BSCT thick films were investigated with variation of the $Dy_2O_3$ amount. As a result of the differential thermal analysis (DTA), the exothermic peak was observed at around $670^{circ}C$ due to the formation of the polycrystalline perovskite phase. All the BSCT thick films showed the XRD patterns of a typical polycrystalline perovskite structure. The average grain size of BSCT thick films decreased with an increasing amount of $Dy_2O_3$. The relative dielectric constant and dielectric loss of the BSCT thick film doped $Dy_2O_3$ 0.1mol% were 4637.4 and 1.6% at 1kHz, respectively.