Red color OLED has been fabricated by the doping method apply to CBP using co-evaporation, GDI4349 of phosphorescent dopant, and rubrene of fluorescent dopant. The OLED structure are multi-layer of ITO(150 nm)/ELM_HIL(50 nm)/ELM_HTL(30 nm)/CBP : Rubrene, GDI4349 (30 nm)/BAlq (30 nm)/LiF(0.7 nm)/Al (100 nm). Accomplished best result at 3 vol.% of rubrene when the OLEDs were made of 1, 3, 5, 7, 9 vol.% doped rubrene. The highest efficiency of 7.2 cd/A was resulted at 8 vol.% of GDI4349 when the OLEDs were made among 5, 8, 11, 14 vol.% of GDI4349. Obviously, the best concentration of rubrene at 3 vol.% and changing GDI4349 concentration to 5, 8, 11, 14 vol.% OLED dramatically enhanced characteristic of resulted 10.7 cd/A at 8 vol.% of GDI4349. This result would understand to analyse as the emission efficiency increases by energy transport efficiency increase using GDI4349 energy transfer when rubrene absorbs the energy from CBP of fluorescences host.