The mechanical properties of $MoSi_2$ based composites containing various types of reinforcement, such as SiC, $ZrO_2$, and W, were investigated, based on detailed examinations of their microstructures. $MoSi_2$ based composites were fabricated at a temperature of $1350^{circ}C$ using a hot-press device. The volume fraction of SiC and $ZrO_2$ particles in this composite system was fixed as 20%. The volume fraction of three types of W particles was changed from 10% to 30%. The characteristics of the $MoSi_2$ based composites were determined by means of optical microscopy and a three-point bending test. The addition of W particles to the $MoSi_2$ powders exhibited a sufficient improvement in the microstructure and mechanical property of the sintered $MoSi_2$ materials, compared to those of SiC and $ZrO_2$ particles. In particular, W/$MoSi_2$ composites containing W particles of 20 vol% represented a good flexural strength of about 530MPa at room temperature, accompanying a relative density of about 92%. The flexural strength of the W/$MoSi_2$ composites tended to decrease with an increase in the average size of the W particles.