Influences of ceramic filler types and dose on the sintering, phase evolution, and dielectric properties of ceramic/CaO-$Al_2O_3-SiO_2$ glass composites were investigated. All of the specimens were sintered at $900^{circ}C$ for 2 h, which conditions are required by the lowtemperature co-firing ceramic (LTCC) technology. Ceramic fillers of $Al_2O_3,;SiO_2$, kaolin, and wollastonite were used. The addition of $Al_2O_3$ filler yielded the crystalline phases of alumina and wollastonite, and the densification over 95% of the relative density was achieved up to 50 wt% addition of the filler. For the cases of the fillers of $SiO_2$, kaolin, and wollastonite, crystalline phases of quartz, mullite, and wollastonite formed, while the densification decreased monotonically with the filler addition. In overall, all the investigated fillers with 10 wt% addition resulted in a reasonable sintering (over 95 %) and low dielectric constants (less than 6), demonstrating the feasibility of the investigated composites for application to a LTCC substrate material with a low dielectric constant.