The superlattice infrared photodetector (SLIP) with an active layer of 8/8-ML InAs/GaSb type-II strained-layer superlattice (SLS) of 150 periods was grown by MBE technique, and the proto-type discrete device was defined with an aperture of $200-{mu}m$ diameter. The contrast profile of the transmission electron microscope (TEM) image and the satellite peak in the x-ray diffraction (XRD) rocking curve show that the SLS active layer keeps abrupt interfaces with a uniform thickness and a periodic strain. The wavelength and the bias-voltage dependences of responsivity (R) and detectivity ($D^*$) measured by a blackbody radiation source give that the cutoff wavelength is ${sim}5{mu}m$, and the maximum Rand $D^*$ ($lambda=3.25{mu}m$) are ${sim}10^3mA/W$ (-0.6 V/13 K) and ${sim}10^9cm.Hz^{1/2}/W$ (0 V/13 K), respectively. The activation energy of 275 meV analyzed from the temperature dependent responsivity is in good agreement with the energy difference between two SLS subblevels of conduction and valence bands (HH1-C) involving in the photoresponse process.