This research was performed to purify water quality through removing T-N, and T-P and to estimating rate of $NO_x$ by the response of photocatalyst using ceramics. The ceramics was a mixtures of Titanium Diboride($TiB_2$) which is used to develop armored cars with excellent protective power and lightness, Olivine, and Hwangto with water and was furnaced for an hour at $1160^{circ}C$. Hwangto and Olivine used in the study are produced at Haenam-gun, Jeonnam, and Andong-city, Gyeongsangbuk-do, respectively. The ground Hwangto and Olivine were seived through PR $100{ imes}200$, and $TiB_2$ was a product of SIGMA ALDRICH. The experiment was performed under the sunlight, Mass flow controller was used for constant flow to pass through the pyrex reactor which was fully charged with furnaced ceramics. The concentration of $NO_2$ gas passed through the pyrex reactor was measured by Multi Gas Monitor. The reaction took for 60 minutes, The material was exposed to sunlight for 40 minutes. The sunlight was interrupted before and after the exposure for 10 minutes. The result showed that the concentration of $NO_2$ gas of the ceramics with $TiB_2$ and without $TiB_2$ became reduced and then maintained the same concentration under the sunlight, and became increased when the sunlight is interrupted. The $NO_2$ removing efficiency of the ceramics mixed with $TiB_2$ was 14~43% higher than that of the ceramics without $TiB_2$ under the sunlight. The study showed that the removing rate of $NO_2$ was 80% when the mixture rate of Hwangto, Olivine, and $TiB_2$ was 68%, 30% and 2%.