The thermoluminescent phosphors of LiYSi$O_4$ containing rare earth metal(La) dopants of 1 wt.%5 wt.% were prepared, and their TL characteristics have been investigated as a function of parameters such as the doping level and the heating rate. The grain size and cooling temperature of the highly sensitive LiYSi$O_4$: La phosphors have been investigated. The glow curve of LiYSi$O_4$: La has two peaks ($P_1,;P_2$), and the peak height ratio of the two peaks is called $P_2/P_1$; here, the main peak is $P_2$. Experimental results indicate that the peak height ratios of the glow curve for LiYSi$O_4$: La are clearly correlated with the grain size and cooling temperature. The maximum $P_2/P_1$ ratio 3.25, the maximum sensitivity was observed for a grain size between 100-150 ${mu}m$. The intensity of the TL peak of the phosphors was linearly proportion to the dose of X-rays.