When scouring and contraction finishing at $90^{circ}C$ using Relaxer or Rotary Washer contraction and weight loss ratio in warp and weft directions were excellent. Also surface state of fabric after drying or sanding treatment was excellent without crease. Low melting polyester fabric showed a complete melting bond by heat setting(P/S) at above $160^{circ}C$. The alkali hydrolysis reaction of polyester showed the breakpoint in the weight loss behavior test, polyester yarn showed a breakpoint ranging from 25% to 28%. This is due to the difference of the hydrolysis rate between regular polyester and soluble polyester. Initially the soluble polyester was eluted and micro-fibrillized 5 times faster than a regular polyester. At a later time, a regular polyester was reduced weight to impart a proper flexibility and drape property to the fabric. As a result of surface sanding finishing, the surface of interior fabric showed a surface state most stabilized when using Mesh No. 220 in mono 0.2d after elution finishing. When the rotation direction of sanding roller was pro-, pro-, pro-, and retro-direction, a directional effect of tuft was not shown, a writing effect as suede was exhibited and a surface state was even. Sublimation fastness was 3-4 class for polyester and 2-4 class for nylon. Light fastness 3-4 class after lapse of 100 hours and 2-4 class after lapse of 160 hours. Abrasion fastness was 3-4 class on wet and 4-5 class on dry Laundry fastness was 2-4 class. As such, the abrasion fastness is slightly reduced upon wetting and the use thereof for interior is excellent, whereas laundry fastness is slightly lowered.