Superplastic deformation behavior and texture evolution after equal channel angular pressing (ECAP) of Zn-0.3Wt%Al alloy were investigated in this study. ECAP was conducted at temperatures from $60^{circ}C$ to $160^{circ}C$ on the plate type specimens of 5 mm thickness and 20 mm width. The specimens obtained by ECAP showed typical texture with basal poles tilted away from the ND toward ED, which is called shear texture. Tensile tests were carried out at $100^{circ}C$ for ECAPed specimens under the strain rate of 0.0002/s. After ECAP of the Zn-0.3Wt%Al alloy, elongation was dramatically increased up to 500% at $100^{circ}C$. The effect of ECAP on the anisotropy in the superplastic deformation behavior was negligible.