The pure crystalline $Li_{1.1}V_{0.9}O_2$ powder has been prepared by a simple solid state reaction of $Li_2CO_3$ and $V_2O_3$ precursors under nitrogen gas containing 10 mol % hydrogen gas flow. The structure of $Li_{1.1}V_{0.9}O_2$ powder was analyzed using Xray diffraction (XRD) and scanning electron microscope (SEM). The stoichiometric $Li_{1.1}V_{0.9}O_2$ powder was used as anode active material for lithium secondary batteries. Its electrochemical properties were investigated by cyclic voltammetry and constant current methods using lithium foil electrode. The observed specific discharge capacity and charge capacity were 360 mAh/g and 260 mAh/g during the first cycle, respectively. In addition, the cyclic efficiency of this cell was 72.2% in the first cycle. The specific capacity of $Li_{1.1}V_{0.9}O_2$ anode rapidly declines as the current rate increases and retains only 30 % of the capacity of 0.1C rate at 1C rate. The crystallinity of the $Li_{1.1}V_{0.9}O_2$ anode decrease as discharge reaction proceeds. However, the relative intensity of main peaks was almost recovered when the cell was charged up to 1.5 V.