Anodic aluminum oxide (AAO) nanotemplates for nano electronic device applications have been attracting increasing interest because of ease of fabrication, low cost process, and possible fabrication in large area. The size and density of the nanostructured materials can be controlled by changing the pore diameter and the pole density of AAO nanotemplate. In this paper, nano porous alumina films AAO nanotemplate was fabricated by second anodization method using sputterd Al films. In addition, effects of electrolyte temperature and anodization voltate on the microstructure of porous alumina films were investigated. As the electrolyte temperature was increased from $8^{circ}C$ to $20^{circ}C$, the growth rate of nanoporous alumina films was increased from 86.2 nm/min to 179.5 nm/min. The AAO nanotemplate fabricated with optimal condition had the mean pore diameter of 70 nm and the pore depth of $1;{mu}m$.